PRODUCT DETAILS
    • Base: Soft Monomeric Calendared PVC Film
    • Base Thickness: 4 mil or 100 microns (± 5 micron)
    • Finished product weight: 290 ± 20 gsm
    • Surface Finish: GLOSS or MATTE
    • Adhesive: Permanent Clear solvent acrylic adhesive
    • Rlease Liner: 140 gsm single side PE coated siliconized paper liner
    • Initial Adhesion: 9-12 N / inch
    • Ink Compatibility: Eco-solvent & Solvent inks
    • Ink Limit: Around 350% with original inks
    • Weathering: Two Years to Two and Half Year
HIGHLIGHTS 
  • 4 mil Base provides thick base for easy handling of substrate.
  • High Gloss & Pure Matte PVC base makes this film excellent for signage.
  • High ink limit ensures vibrant color gamut and vivid displays.
  • Natural whiteness for high color contrast.
  • Good sheet stability & lay flatness for ease of conversion and application
  • Excellent adhesion to a variety of substrates for wide range of applications
  • Siliconized double sided PE coated paper liner for excellent flatness or 100% P.E.T. liner
TECHNICAL DETAILS 
PROPERTY  TEST METHOD RESULTS
Dimensional Stability FINAT TM14

 Adhered to Steel, no shrinkage in cross direction.         In length 0.50mm max

Temp. Resistance    Adhered to Aluminium. -20°C to +65°C. No Variation.
Seawater Resistance DIN 50021  Adhered to glass, after 48h/23°C, No Variation
Adhesive Strength FINAT TM1  After 24hour, stainless steel, 8~12N/25 mm
Tensile Strength  
along

D882-02; 200mm/min

 Min. 24 Mpa
across  Min. 23 Mpa
Elongation at Break  
along D882-02; 200mm/min  Min 140%
across  Min 180%
Weathering   Two Years to Two & Half years
  • Compatible with original solvent & eco-solvent inks from printers of HP series, Epson series, HP Latex series, Roland series, Mutoh series, Mimaki JV series & wide range of UV printers.
  • Compatible with HP LATEX printers as well. However, HP 1st Gen Latex printers suggested to test the product before proceeding with production run.
  • Use standard vinyl inks. Print image on vinyl, not on the release liner.